| Bonding Function: | Instant Adhesive |
|---|---|
| Application: | Construction |
| Material: | Polyurethane |
|
Still deciding? Get samples of US$ 0/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
|
Part A Curing Agent
|
Part B Main Agent
|
|
Appearance: Clear liquid
|
Appearance: liquid (RAL color available) |
|
Viscosity 25ºC: 2000 CPS (±200 CPS)
|
Viscosity 25ºC:2500 CPS (±200 CPS)
|
|
Density (KG/L): 1.01
|
Density(KG/L): 1.06
|
|
Solids: 100%
|
Solids: 95%
|
|
Material properties after curing
|
|
|
Paint appearance
|
Liquid
|
|
7 days hardness
|
shore D 68
|
|
Abrasion (CS17 wheel 750g, 500 rpm)
|
25mg
|
|
Tensile strength (MPa)
|
10
|
|
Concrete adhesion (Mpa)
|
2.2
|
|
Impact resistance (1000g, 1m)
|
Pass
|
|
Baoli Polyaspartic resin
|
Epoxy resin
|
|
It has little effect on temperature change, and can be operated normally and dried quickly (30min-5h) under the environment of -15ºC to 40ºC and humidity ≤85%.
|
Low temperature construction is difficult, the need for external heating assisted construction, low temperature curing trapped (above 48hours) |
|
Environmental protection, low temperature, VOC controllable, construction solid content (70%-100%)
|
The curing agent of epoxy coatings is a small molecular weight amine substance, so the odor is bad and the volatile components are large. |
|
Good color retention and UV resistance linear, outdoor use for 15 years does not change color, does not powder
|
Poor color retention and UV resistance, easy to crack, warping and delamination.
|
|
Elastic adjustable,which rigid materials have good hardness and a certain degree of flexibility,
|
Only rigid coatings can be prepared, and the flexibility is poor
|
|
Wear resistance and impact resistance superior
|
No impact resistance nor wear resistance, easy to delamination by external impact
|